Corundum Brick

Corundum Brick

High Purity Corundum Brick (HPA) contain tabular alumina as the base grain and may include various fine materials such as calcined alumina, clay and fine silica. As these bricks generally have low impurity levels, alumina and silica typically make up 99% of the chemical composition. Usually, the only mineral phases present are corundum and mullite. Properties such as high hot strength, creep and slag resistance benefit from this purity level.

 

HPA made primarily of alumina under medium to high temperature burning, HPA has advantages such as high purity, strength, chemical stability and corrosion resistance. It was widely used as internal lining of petrochemical and instrument equipment such as ammonia gasifier, ethylene gasifier and carbon black reactor, in which high temperature, pressure, chemical corrosion and mechanical abrasion is encountered.

 

Corundum Brick01 www.osymen.com Corundum Brick02 www.osymen.com

Corundum Brick03 www.osymen.com Corundum Brick04 www.osymen.com

Corundum Brick05 www.osymen.com Corundum Brick07 www.osymen.com

Corundum Brick09 www.osymen.com Corundum Brick010 www.osymen.com

OSYMEN BRAND

Al2O3

SiO2

Fe2O3

A.P

B.D

CCS

PLC

RUL

1600oCX2h

%

%

%

%

g/cm3

MPa

%

oC

HPA-90

90.0

8.00

0.20

17.0

3.00

80

0.2

1700

HPA-95

95.0

3.50

0.20

18.0

3.10

80

-0.3~+0.3

1700

HPA-98

98.0

0.50

0.20

19.0

3.15

80

-0.2~+0.2

1700

HPA-99A

99.5

0.15

0.10

19.0

3.20

80

-0.2~+0.2

1700

HPA-99B

99.1

0.10

0.15

19.0

3.20

80

-0.2~+0.2

1700

AP: Apparent Porosity   |  BD: Bulk Density  |  CCS: Cold Crushing Strength  |  RUL: Refractories Under Load  |  PLC: Permanent Linear Change | TSR : Thermal Shock Resistance

Last updated: 2024-01-03