Low Creep High Alumina Brick for Hot Blast Stove

Low Creep High Alumina Brick for Hot Blast Stove

Low Creep High Alumina Brick for Hot Blast Stove is made of corundum, mullite “sillimanite, andalusite and kyanite” and high-quality bauxite clinker as raw material by shaping at high pressure and sintering at high temperature.


Low Creep High Alumina Brick for Hot Blast Stove Characteristic:
1. The content of AL2O3 is ≥48%.

2. High refractoriness. The temperature is up to 1750~1790 oC, it belongs to high-duty refractory.
3. High refractoriness under load. The URL is higher than fireclay brick as the high content of Al2O3, however, it is lower than silica brick because of mullite crystal does not form reticular tissue.
4. Excellent slag resistance. High alumina brick is a kind of neutral refractory material so it enjoys excellent resistance to acid slag and alkali slag corrosion.

Low Creep High Alumina Brick for Hot Blast Stove Application:
The main markets for low creep high alumina brick are building lining of hot-blast stove, blast furnace, coke oven, rotary kilns of cement and so on.

 

OSYMEN BRAND

Al2O3

A.P

B.D

CCS

PLC

Creep

(0.2MPa, 0~50h)

1450oCX2hrs

1500oCX2hrs

%

%

g/cm3

MPa

%

%

%

DRL-127

50.0

23

2.30-2.50

50

-0.3~0.2

 

1270 oC
0.8

DRL-130

60.0

22

2.30-2.50

55

-0.3~0.2

 

1300 oC
0.8

DRL-135

65.0

22

2.35-2.55

55

-0.3~0.2

 

1350 oC
0.8

DRL-140

65.0

22

2.40-2.60

55

-0.2~0.2

 

1400 oC
0.8

DRL-145

65.0

21

2.50-2.70

60

 

-0.2~0.2

1450 oC
0.8

DRL-150

75.0

21

2.60-2.85

60

 

-0.2~0.2

1500 oC
0.8

DRL-155

75.0

20

2.60-2.85

60

 

-0.2~0.2

1550oC
0.8

AP: Apparent Porosity   |  BD: Bulk Density  |  CCS: Cold Crushing Strength  |  RUL: Refractories Under Load  |  PLC: Permanent Linear Change