Fused Cast Brick

  • FUSED CAST AZS 41

    FUSED CAST AZS 41

    Fused Cast AZS 41 has the most free baddeleyite crystals among the AZS families, which are evenly distributed within the block. Its corrosion resistibility is the best and thus it is usually recommended to be used in the most demanding positions to balance the furnace life.

    More+

    Fused Cast AZS 41 has the most free baddeleyite crystals among the AZS families, which are evenly distributed within the block. Its corrosion resistibility is the best and thus it is usually recommended to be used in the most demanding positions to balance the furnace life.

    OSYMEN BRAND

    AZS41# ER1711

    Al2O%

    Balance

    ZrO2 %

    40-44

    SiO2 %

    ≤12.50

    Na2O %

    ≤1.25

    Fe2O3+TiO2+CaO+Na2O %

    ≤2.5

    True Specific Gravity, g/cm3

    ≥4.10

    Bulk Density, g/cm3    PT (RN RC N)

    ZWS (RR EVF EC ENC)
    WS (RT VF EPIC FVP DCL) 

    ≥3.55

    ≥3.85

    ≥3.95

    Apparent Porosity, %

    ≤0.9

    Cold crushing strength, Mpa

    ≥350

    Exudation Temperature of Glass Phase, °C

    ≥1400

    Refractoriness under Load T2 , °C

    ≥1700

    Bubble Separation Ratio(1300°C×10h), %

    ≤1.0

    Anti-corrosion rate of glass liquid

    1500°C×36h (mm/24h), %

    ≤1.2

    Close
  • FUSED CAST AZS 36

    FUSED CAST AZS 36

    Besides the same eutectic with AZS 33 Tile, FUSED CAST AZS 36 Tile has further strengthened anti-erosion ability and reduces the pollution of glass melt because more chain-shape zirconium oxide crystal and low glass phase content. It is suitable for the area with fast glass melt flow rate and high temperature, such as pool wall tiles of the melting tank, pavement tiles and charging mouth tiles.

    More+

    Besides the same eutectic with AZS 33 Tile, FUSED CAST AZS 36 Tile has further strengthened anti-erosion ability and reduces the pollution of glass melt because more chain-shape zirconium oxide crystal and low glass phase content. It is suitable for the area with fast glass melt flow rate and high temperature, such as pool wall tiles of the melting tank, pavement tiles and charging mouth tiles.

    OSYMEN BRAND

    AZS36# ER1685

    Al2O3 %

    Balance

    ZrO2 %

    35-40

    SiO2 %

    ≤13.00

    Na2O %

    ≤1.40

    Fe2O3+TiO2+CaO+Na2O %

    ≤2.5

    True Specific Gravity, g/cm3

    ≥3.93

    Bulk Density, g/cm3    PT (RN RC N)

    ZWS (RR EVF EC ENC)
    WS (RT VF EPIC FVP DCL) 

    ≥3.50

    ≥3.70

    ≥3.80

    Apparent Porosity, %

    ≤1.0

    Cold crushing strength, Mpa

    ≥350

    Exudation Temperature of Glass Phase, °C

    ≥1400

    Refractoriness under Load T2 , °C

    ≥1700

    Bubble Separation Ratio(1300°C×10h), %

    ≤1.4

    Anti-corrosion rate of glass liquid

    1500°C×36h (mm/24h), %

    ≤1.4

    Close
  • FUSED CAST AZS 33

    FUSED CAST AZS 33

    The compact microstructure of Fused Cast AZS 33 enables it to have very good corrosion resistance to molten glass. It very rarely results in stoning and has very limited chances to cause blistering and other defects to glass, so AZS 33 is the most common product used in the glass furnace

    More+

    The compact microstructure of Fused Cast AZS 33 enables it to have very good corrosion resistance to molten glass. It very rarely results in stoning and has very limited chances to cause blistering and other defects to glass, so AZS 33 is the most common product used in the glass furnace

    OSYMEN BRAND

    AZS33# ER1681

    Al2O3 %

    Balance

    ZrO2 %

    32-36

    SiO2 %

    ≤15.30

    Na2O %

    ≤1.40

    Fe2O3+TiO2+CaO+Na2O %

    ≤2.5

    True Specific Gravity, g/cm3

    ≥3.84

    Bulk Density, g/cm3    PT (RN RC N)

    ZWS (RR EVF EC ENC)
    WS (RT VF EPIC FVP DCL) 

    ≥3.45

    ≥3.60
    ≥3.70

    Apparent Porosity, %

    ≤1.2

    Cold crushing strength, Mpa

    ≥350

    Exudation Temperature of Glass Phase, °C

    ≥1400

    Refractoriness under Load T2 , °C

    ≥1700

    Bubble Separation Ratio(1300°C×10h), %

    ≤2.0

    Anti-corrosion rate of glass liquid

    1500°C×36h (mm/24h), %

    ≤1.45

    Close
Last updated: 2024-01-03